CWB Level 2 Exam Questions and Answers
2025 – Complete Study Set REAL EXAM!!!
1.To measure the strength of a welded joint what mechanical test would you prescribe?
a) A trANSWERverse weld tension test
b) A charpy test.
c) A CTOD test.
d) An all weld metal tension test. e) A side bend test. - ANSWER ✔---a) A trANSWERverse weld
tension test
2. Select the cutting process that would provide the narrowest heat affected zone when cutting 12.5
mm (0.5 in) thick carbon steel.
a) Oxy-acetylene cutting.
b) Air-carbon arc cutting.
c) Oxy-propane cutting.
d) Plasma arc cutting.
e) Laser beam cutting - ANSWER ✔---e) Laser beam cutting
3. Which of the following refers to a welder test where a pipe assembly is placed vertically and the joint
welded in the horizontal position without rotating the assembly?
a) 1G
,b) 2G
c) 3G
d) 5G
e) 6G - ANSWER ✔---b) 2G
4. Which of the following imperfections is normally considered as unacceptable regardless of size or
location?
a) Porosity.
b) Crack.
c) Inadequate penetration.
d) Lamination.
e) Burn-through. - ANSWER ✔---b) Crack.
5. Select the correct penetrameter thickness for 2% sensitivity when radiographing a weldment 1 .25
inches in thickness.
a) 0.012 in.
b) 0.015 in.
c) 0.025 in
d) 0.030 in. - ANSWER ✔---c) 0.025 in
6. Which of the following statements concerning porosity is true?
a) Porosity cannot be trapped within a weld.
b) Porosity moves up through later passes and will show only in a final pass.
c) Porosity is restricted to the centre line of a weld.
d) Porosity can result from faulty welder technique.
e) Porosity can be dissipated by an appropriate heat treatment. - ANSWER ✔---d) Porosity can result
from faulty welder technique.
7. An irregular, dense white spot is seen on the radiograph of a weld. Assuming it was caused by the
welding process used, which one of the processes below would be responsible?
, a) SMAW process.
b) GTAW process.
c) GMAW process.
d) ST process.
e) ESW process. - ANSWER ✔---b) GTAW process.
8. Which of the following operations is known to result in the emission of ionizing radiation at levels
dangerous to human health?
A) shield metal arc welding.
B) Plasma arc welding.
C) Operation of high voltage portable generator sets.
d) Radiographic inspection.
e) Electroslag and electrogas welding. - ANSWER ✔---d) Radiographic inspection.
9. The ultrasonic trANSWERducer is pressed against the plate of a welded joint. The sound travels
longitudinally through the plate to the opposite side. The signal seen on the UT screen that comes from
this opposite side of the plate:
a) Is the initial pulse signal.
b) Is the back reflection signal.
c) Is the front reflection signal.
d) Must be equal in amplitude to any defect signal.
e) Cannot be used for establishing the thickness of the material under test. - ANSWER ✔---b) Is the
back reflection signal.
11. Which of the following is a stainless steel electrode?
a) E4918-1
b) E4918-A1
c) E4818
d) E308-16
e) E4111 - ANSWER ✔---d) E308-16
2025 – Complete Study Set REAL EXAM!!!
1.To measure the strength of a welded joint what mechanical test would you prescribe?
a) A trANSWERverse weld tension test
b) A charpy test.
c) A CTOD test.
d) An all weld metal tension test. e) A side bend test. - ANSWER ✔---a) A trANSWERverse weld
tension test
2. Select the cutting process that would provide the narrowest heat affected zone when cutting 12.5
mm (0.5 in) thick carbon steel.
a) Oxy-acetylene cutting.
b) Air-carbon arc cutting.
c) Oxy-propane cutting.
d) Plasma arc cutting.
e) Laser beam cutting - ANSWER ✔---e) Laser beam cutting
3. Which of the following refers to a welder test where a pipe assembly is placed vertically and the joint
welded in the horizontal position without rotating the assembly?
a) 1G
,b) 2G
c) 3G
d) 5G
e) 6G - ANSWER ✔---b) 2G
4. Which of the following imperfections is normally considered as unacceptable regardless of size or
location?
a) Porosity.
b) Crack.
c) Inadequate penetration.
d) Lamination.
e) Burn-through. - ANSWER ✔---b) Crack.
5. Select the correct penetrameter thickness for 2% sensitivity when radiographing a weldment 1 .25
inches in thickness.
a) 0.012 in.
b) 0.015 in.
c) 0.025 in
d) 0.030 in. - ANSWER ✔---c) 0.025 in
6. Which of the following statements concerning porosity is true?
a) Porosity cannot be trapped within a weld.
b) Porosity moves up through later passes and will show only in a final pass.
c) Porosity is restricted to the centre line of a weld.
d) Porosity can result from faulty welder technique.
e) Porosity can be dissipated by an appropriate heat treatment. - ANSWER ✔---d) Porosity can result
from faulty welder technique.
7. An irregular, dense white spot is seen on the radiograph of a weld. Assuming it was caused by the
welding process used, which one of the processes below would be responsible?
, a) SMAW process.
b) GTAW process.
c) GMAW process.
d) ST process.
e) ESW process. - ANSWER ✔---b) GTAW process.
8. Which of the following operations is known to result in the emission of ionizing radiation at levels
dangerous to human health?
A) shield metal arc welding.
B) Plasma arc welding.
C) Operation of high voltage portable generator sets.
d) Radiographic inspection.
e) Electroslag and electrogas welding. - ANSWER ✔---d) Radiographic inspection.
9. The ultrasonic trANSWERducer is pressed against the plate of a welded joint. The sound travels
longitudinally through the plate to the opposite side. The signal seen on the UT screen that comes from
this opposite side of the plate:
a) Is the initial pulse signal.
b) Is the back reflection signal.
c) Is the front reflection signal.
d) Must be equal in amplitude to any defect signal.
e) Cannot be used for establishing the thickness of the material under test. - ANSWER ✔---b) Is the
back reflection signal.
11. Which of the following is a stainless steel electrode?
a) E4918-1
b) E4918-A1
c) E4818
d) E308-16
e) E4111 - ANSWER ✔---d) E308-16