CWB 1 Exam Q-Bank | Actual Questions
& Certified Solutions | Complete
Accurate Quizzes with Verified
Answers | 2025-2026.
_____________Quiz____________?
1. Which is not a recommended method for surface cleaning of a part for liquid penetrant
examination?
a) Cleaning with organic solvents.
b) Blasting with shot or dull sand.
c) Cleaning with de-greasers.
d) Use of de-scaling solutions.
e) Ultrasonic cleaning methods. -
Answer✓✓
b) Blasting with shot or dull sand.
_____________Quiz____________?
2. Which of the following weld defects is most likely to be missed by radiography in a weld:
a) Undercutting.
b) Porosity.
c) Slag inclusions.
d) Cracking.
e) Burn through . -
1
, Answer✓✓
d) Cracking.
_____________Quiz____________?
3. In the choices given below, metallographic tests would be the least informative with regard
to the:
a) Presence of the non-metallic inclusions.
b) Grain structure in the weld and fusion zone.
c) Ability of the material to withstand repeated fluctuating loads.
d) Extent and structure of the heat affected zone.
e) Number of weld passes. -
Answer✓✓
c) Ability of the material to withstand repeated fluctuating loads.
_____________Quiz____________?
4. In producing a drawing for a scale of 1:50, what would be the distance represented by a
distance on
the drawing of 6 em?
a) 12 cm.
b) 30 cm.
c) 50 cm.
d) 240 cm.
e) 300 cm. -
2
, Answer✓✓
e) 300 cm.
_____________Quiz____________?
5. The mechanical test used to determine the ability of a material to resist failure by brittle
fracture
requires the use of:
a) A tensile test specimen.
b) A bend test specimen.
c) A compression test specimen.
d) An impact test specimen.
e) A spectrographic test. -
Answer✓✓
d) An impact test specimen.
_____________Quiz____________?
6. The cooling rate of aT-joint is:
a) Less than that in a butt joint.
b) Greater than that in a butt joint.
c) Greater than that in a butt joint only where the carbon equivalent is high .
d) Greater at the mid-section than at the start.
e) Greater at the mid-section than at the finish. -
Answer✓✓
3
, b) Greater than that in a butt joint.
_____________Quiz____________?
7. What are slag and non-metallic inclusions usually caused by?
a) Moisture in the weld joint.
b) High welding current.
c) Loss of shielding gas.
d) Inadequate interpass cleaning. -
Answer✓✓
d) Inadequate interpass cleaning.
_____________Quiz____________?
8. Where deviations from the drawings are warranted the inspector should do which of the
following?
a) Authorize approval of the changes.
b) Obtain official approval for the changes.
c) Reject the work without any further consideration.
d) Stop the work until drawing revisions have been completed. -
Answer✓✓
b) Obtain official approval for the changes.
_____________Quiz____________?
4
& Certified Solutions | Complete
Accurate Quizzes with Verified
Answers | 2025-2026.
_____________Quiz____________?
1. Which is not a recommended method for surface cleaning of a part for liquid penetrant
examination?
a) Cleaning with organic solvents.
b) Blasting with shot or dull sand.
c) Cleaning with de-greasers.
d) Use of de-scaling solutions.
e) Ultrasonic cleaning methods. -
Answer✓✓
b) Blasting with shot or dull sand.
_____________Quiz____________?
2. Which of the following weld defects is most likely to be missed by radiography in a weld:
a) Undercutting.
b) Porosity.
c) Slag inclusions.
d) Cracking.
e) Burn through . -
1
, Answer✓✓
d) Cracking.
_____________Quiz____________?
3. In the choices given below, metallographic tests would be the least informative with regard
to the:
a) Presence of the non-metallic inclusions.
b) Grain structure in the weld and fusion zone.
c) Ability of the material to withstand repeated fluctuating loads.
d) Extent and structure of the heat affected zone.
e) Number of weld passes. -
Answer✓✓
c) Ability of the material to withstand repeated fluctuating loads.
_____________Quiz____________?
4. In producing a drawing for a scale of 1:50, what would be the distance represented by a
distance on
the drawing of 6 em?
a) 12 cm.
b) 30 cm.
c) 50 cm.
d) 240 cm.
e) 300 cm. -
2
, Answer✓✓
e) 300 cm.
_____________Quiz____________?
5. The mechanical test used to determine the ability of a material to resist failure by brittle
fracture
requires the use of:
a) A tensile test specimen.
b) A bend test specimen.
c) A compression test specimen.
d) An impact test specimen.
e) A spectrographic test. -
Answer✓✓
d) An impact test specimen.
_____________Quiz____________?
6. The cooling rate of aT-joint is:
a) Less than that in a butt joint.
b) Greater than that in a butt joint.
c) Greater than that in a butt joint only where the carbon equivalent is high .
d) Greater at the mid-section than at the start.
e) Greater at the mid-section than at the finish. -
Answer✓✓
3
, b) Greater than that in a butt joint.
_____________Quiz____________?
7. What are slag and non-metallic inclusions usually caused by?
a) Moisture in the weld joint.
b) High welding current.
c) Loss of shielding gas.
d) Inadequate interpass cleaning. -
Answer✓✓
d) Inadequate interpass cleaning.
_____________Quiz____________?
8. Where deviations from the drawings are warranted the inspector should do which of the
following?
a) Authorize approval of the changes.
b) Obtain official approval for the changes.
c) Reject the work without any further consideration.
d) Stop the work until drawing revisions have been completed. -
Answer✓✓
b) Obtain official approval for the changes.
_____________Quiz____________?