1 (8179) - In Gas Tungsten Arc (GTA) welding, a stream of inert gas is used to A- prevent
the formation of oxides in the puddle.
2 (8180) - Which statement best describes magnesium welding? C- Filler rod should be
the same composition as base metal.
3 (8181) - Which statement is true in regard to welding heat-treated magnesium? A- The
welded section does not have the strength of the original metal.
4 (8182) - The oxyacetylene flame for silver soldering should be B- neutral.
5 (8183) - Why is it necessary to use flux in all silver soldering operations? A- To
chemically clean the base metal of oxide film.
6 (8184) - Engine mount members should preferably be repaired by using a B- larger
diameter tube with fishmouth and rosette welds.
7 (8185) - What method of repair is recommended for a steel tube longeron dented at a cluster?
C- Welded patch plate.
, 8 (8186) - Welding over brazed or soldered joints is A- not permitted.
11 (8189) - Which of the following can normally be welded without adversely affecting
strength?1. Aircraft bolts.2. SAE 4130 chrome/molybdenum tubing.3. Spring steel struts.4. Most
heat-treated steel/nickel alloy components. C- 2
12 (8190) - In selecting a torch tip size to use in welding, the size of the tip opening determines
the A- amount of heat applied to the work.
13 (8191) - Why should a carburizing flame be avoided when welding steel? B- It hardens
the surface.
14 (8192) - The most important consideration(s) when selecting welding rod is B-
material compatibility.
15 (8193) - The oxyacetylene flame used for aluminum welding should A- be neutral and
soft.
16 (8194) - A very thin and pointed tip on a soldering copper is undesirable because it will
C- cool too rapidly.
Answers 100% Verified
1 (8179) - In Gas Tungsten Arc (GTA) welding, a stream of inert gas is used to A- prevent
the formation of oxides in the puddle.
2 (8180) - Which statement best describes magnesium welding? C- Filler rod should be
the same composition as base metal.
3 (8181) - Which statement is true in regard to welding heat-treated magnesium? A- The
welded section does not have the strength of the original metal.
4 (8182) - The oxyacetylene flame for silver soldering should be B- neutral.
5 (8183) - Why is it necessary to use flux in all silver soldering operations? A- To
chemically clean the base metal of oxide film.
6 (8184) - Engine mount members should preferably be repaired by using a B- larger
diameter tube with fishmouth and rosette welds.
7 (8185) - What method of repair is recommended for a steel tube longeron dented at a cluster?
C- Welded patch plate.
, 8 (8186) - Welding over brazed or soldered joints is A- not permitted.
11 (8189) - Which of the following can normally be welded without adversely affecting
strength?1. Aircraft bolts.2. SAE 4130 chrome/molybdenum tubing.3. Spring steel struts.4. Most
heat-treated steel/nickel alloy components. C- 2
12 (8190) - In selecting a torch tip size to use in welding, the size of the tip opening determines
the A- amount of heat applied to the work.
13 (8191) - Why should a carburizing flame be avoided when welding steel? B- It hardens
the surface.
14 (8192) - The most important consideration(s) when selecting welding rod is B-
material compatibility.
15 (8193) - The oxyacetylene flame used for aluminum welding should A- be neutral and
soft.
16 (8194) - A very thin and pointed tip on a soldering copper is undesirable because it will
C- cool too rapidly.