Practice test ASNT-SNT-TC-1A VT Level I/II- Questions and Answers
1. Weldments Cracks, suckback, undercut, and overlap are disconti-
nuities found in:
2. The Employer In accordance with SNT-TC-1A, certification of visual
NDT personnel is the responsibility of
3. Lamination A discontinuity that is not associated with welds is:
4. The same for a convex fillet weld For a given size of weld, the theoretical throat for a
concave fillet weld is:
5. Less than 90 degrees from the plate Overlap is a weld profile condition where the angle
surface formed at the junction between the weld and base
material is:
6. Inclusions When an ingot is rolled, a lamination can result if it
contains piping or:
7. Education and experience An employer shall establish a qualification and certifi-
Training and testing cation program based on:
Evaluation
8. Stringer Bead The melting and fusing of the filler and base metal into
a straight continuous weld pass is called a:
9. Crater Crack A discontinuity with a small star-shaped pattern where
a weld starts, or stops is usually an indication of:
10. It is simple and relatively inexpen- Visual inspection is the most extensively used inspec-
sive, it does not normally require tion method on weldments because:
special equipment, and it gives im-
portant information about confor-
mity to specifications
1/4
1. Weldments Cracks, suckback, undercut, and overlap are disconti-
nuities found in:
2. The Employer In accordance with SNT-TC-1A, certification of visual
NDT personnel is the responsibility of
3. Lamination A discontinuity that is not associated with welds is:
4. The same for a convex fillet weld For a given size of weld, the theoretical throat for a
concave fillet weld is:
5. Less than 90 degrees from the plate Overlap is a weld profile condition where the angle
surface formed at the junction between the weld and base
material is:
6. Inclusions When an ingot is rolled, a lamination can result if it
contains piping or:
7. Education and experience An employer shall establish a qualification and certifi-
Training and testing cation program based on:
Evaluation
8. Stringer Bead The melting and fusing of the filler and base metal into
a straight continuous weld pass is called a:
9. Crater Crack A discontinuity with a small star-shaped pattern where
a weld starts, or stops is usually an indication of:
10. It is simple and relatively inexpen- Visual inspection is the most extensively used inspec-
sive, it does not normally require tion method on weldments because:
special equipment, and it gives im-
portant information about confor-
mity to specifications