CWI Exam AWS D1.1 Part C Questions and Answers 100% Pass

CWI Exam AWS D1.1 Part C Questions and Answers 100% Pass ER70S-X - What is the suggested filler metal classification for welding ASTM A131 Grade DH32 steel with GMAW ? 3/16 inch - When fillet welding a 3/8 inch stud in the flat position with an E7018 electrode, what diameter electrode must be used? indefinitely, unless not engaged in the process for more than 6 months at a time - How long does welder certification last per AWS D1.1? 5/16 - With a single electrode for SAW what is the maximum size single pass fillet weld that can be deposited in the horizontal welding position when using a prequalified procedure once every 3 years or less, if necessary - How often are visual examinations required for inspectors under AWS D1.1? 10 hours - When stress relieving a weldment at a temperature of 150F below the minimum specified temperature, what is the minimum holding time per inch of thickness 2Brittie Donald, All Rights Reserved © 2025 Need not to be welded full length or removed unless specified by the engineer - Steel backing for welds in statically loaded structures 1/8 inch - The maximum weld reinforcement permitted for a welding procedure qualification on pipe or tubing having a wall thickness of 0.028 inch is: one is for plain carbon steel electrodes and the other one is for low alloy steel electrodes - What is the difference between the AWS A5.1 and AWS A5.5 specifications all of the above - Tack welds incorporated into SAW welds shall also meet the following A change of 5% above the mean amperage for each filler metal diameter used - For GMAW, which is not considered to be an essential variable for the procedure qualification E6010 - Which of the following SMAW electrodes is not included in the F2 group? none, the weld shall merge smoothly with the base metal - How much overlap is allowed on a procedure qualification test coupon? 1/8 inch - What is the maximum root opening for welder qualification testing on CJP tubular butt joints without backing? 32F - What is the lowest temperature at which welding can be done without preheating 1/2 inch thick ASTM A36 carbon steel 3Brittie Donald, All Rights Reserved © 2025 AWS A5.20 - What is the classification of a suitable FCAW filler material for joining ASTM A516 Grade 55 steel none, need not be explored - What plate repair is required when a 3/4 inch long laminar discontinuity is discovered in an oxygen cut edge less than 0 F - Welding shall not be done when the ambient temperature is: 1/4 inch minimum - For prequalified joint B-L2c-S, what is the range of root face dimensions, as fit-up, permitted for a base metal thickness of 1 inch 70 F - What is the minimum preheat and interpass temperature for FCAW on 1/2inch thick ASTM A500 Grade A steel, when the base meta