ZELF
STUITERBALLEN
MAKEN
PO Scheikunde
,Inhoudsopgave
Inleiding....................................................................................................................................... 3
Hypothese.................................................................................................................................... 6
Materiaal en methode.................................................................................................................. 8
Materiaal:................................................................................................................................. 8
Methode:.................................................................................................................................. 8
Materiaal:................................................................................................................................. 9
Methode:.................................................................................................................................. 9
Resultaten.................................................................................................................................. 10
Conclusie................................................................................................................................... 14
Discussie................................................................................................................................... 15
Bibliografie................................................................................................................................. 16
2
, Inleiding
Dit onderzoek gaat over het maken van stuiterballen van natuurlijke rubber, en
daarnaast in welke verhouding deze stuiterbal het hoogst kan stuiteren. Wij gaan hier
voor twee verschillende soorten stuiterballen maken. Dit onderzoek beantwoord de
volgende gecombineerde onderzoeksvraag: ‘Stuitert een stuiterbal van borax en lijm of
een stuiterbal van ethanol en waterglas hoger en in welke verhouding? Met effectief
bedoelen wij de hoogte die de stuiterbal haalt als hij van een vaste hoogte stuitert. Deze
stuiterballen bestaan dus uit waterglas en ethanol of Borax, maizena, water en lijm.
Na het maken van de stuiterballen met verschillende verhoudingen ethanol en
waterglas, zal door een stuiter test worden bepaald welke stuiterbal het beste is. De
ethanol en waterglas reageren tot silica polymeren, er ontstaat een synthetisch rubber.
Polymeren bestaan uit zich herhalende chemische eenheden, monomeren.
Tussen waterglas (natriumsilicaat) en ethanol ontstaat de volge reactievergelijking wat
voor een polymeervorming zorgt.
SiO2 + 2C2H5OH → + H2O
Natriumsilicaat
ontstaat door zand (SiO2) en natriumcarbonaat
(Na2CO3) samen te smelten in een oven bij ongeveer
1300 ° C. Hier uit ontstaat Na2O (SiO2) n, ook wel
waterglas. De reactie met ethylalcohol levert een bal met
stuiterend vermogen op die hoogstwaarschijnlijk een
siliconen elastomeer is, zoals hierboven te zien, de R in
de reactievergelijking staat waarschijnlijk voor -O-CH2CH3, of een andere methylgroep.
Ethanol (2C2H5OH) bestaat uit een koolstofketen (CH)
en een hydroxygroep (OH). OH-moleculen kunnen
waterstofbruggen vormen en zo verschillende ketens
verbinden. De OH-moleculen van ethanol reageren met
de O-moleculen van natriumsilicaat door middel van
condensatiepolymerisatie er ontstaat een binding en
3
STUITERBALLEN
MAKEN
PO Scheikunde
,Inhoudsopgave
Inleiding....................................................................................................................................... 3
Hypothese.................................................................................................................................... 6
Materiaal en methode.................................................................................................................. 8
Materiaal:................................................................................................................................. 8
Methode:.................................................................................................................................. 8
Materiaal:................................................................................................................................. 9
Methode:.................................................................................................................................. 9
Resultaten.................................................................................................................................. 10
Conclusie................................................................................................................................... 14
Discussie................................................................................................................................... 15
Bibliografie................................................................................................................................. 16
2
, Inleiding
Dit onderzoek gaat over het maken van stuiterballen van natuurlijke rubber, en
daarnaast in welke verhouding deze stuiterbal het hoogst kan stuiteren. Wij gaan hier
voor twee verschillende soorten stuiterballen maken. Dit onderzoek beantwoord de
volgende gecombineerde onderzoeksvraag: ‘Stuitert een stuiterbal van borax en lijm of
een stuiterbal van ethanol en waterglas hoger en in welke verhouding? Met effectief
bedoelen wij de hoogte die de stuiterbal haalt als hij van een vaste hoogte stuitert. Deze
stuiterballen bestaan dus uit waterglas en ethanol of Borax, maizena, water en lijm.
Na het maken van de stuiterballen met verschillende verhoudingen ethanol en
waterglas, zal door een stuiter test worden bepaald welke stuiterbal het beste is. De
ethanol en waterglas reageren tot silica polymeren, er ontstaat een synthetisch rubber.
Polymeren bestaan uit zich herhalende chemische eenheden, monomeren.
Tussen waterglas (natriumsilicaat) en ethanol ontstaat de volge reactievergelijking wat
voor een polymeervorming zorgt.
SiO2 + 2C2H5OH → + H2O
Natriumsilicaat
ontstaat door zand (SiO2) en natriumcarbonaat
(Na2CO3) samen te smelten in een oven bij ongeveer
1300 ° C. Hier uit ontstaat Na2O (SiO2) n, ook wel
waterglas. De reactie met ethylalcohol levert een bal met
stuiterend vermogen op die hoogstwaarschijnlijk een
siliconen elastomeer is, zoals hierboven te zien, de R in
de reactievergelijking staat waarschijnlijk voor -O-CH2CH3, of een andere methylgroep.
Ethanol (2C2H5OH) bestaat uit een koolstofketen (CH)
en een hydroxygroep (OH). OH-moleculen kunnen
waterstofbruggen vormen en zo verschillende ketens
verbinden. De OH-moleculen van ethanol reageren met
de O-moleculen van natriumsilicaat door middel van
condensatiepolymerisatie er ontstaat een binding en
3