CWB 1 EXAM QUESTIONS AND ANSWERS 100%
CORRECT AND UPDATED!!
,1. Which is not a recommended method for surface cleaning of a part for liquid
penetrant examination?
a) Cleaning with organic solvents.
b) Blasting with shot or dull sand.
c) Cleaning with de-greasers.
d) Use of de-scaling solutions.
e) Ultrasonic cleaning methods. - ANSWER b) Blasting with shot or dull sand.
2. Which of the following weld defects is most likely to be missed by radiography in a
weld:
a) Undercutting.
b) Porosity.
c) Slag inclusions.
d) Cracking.
e) Burn through . - ANSWER d) Cracking.
3. In the choices given below, metallographic tests would be the least informative with
regard to the:
a) Presence of the non-metallic inclusions.
b) Grain structure in the weld and fusion zone.
c) Ability of the material to withstand repeated fluctuating loads.
d) Extent and structure of the heat affected zone.
e) Number of weld passes. - ANSWER c) Ability of the material to withstand repeated
fluctuating loads.
4. In producing a drawing for a scale of 1:50, what would be the distance represented
by a distance on
the drawing of 6 em?
a) 12 cm.
b) 30 cm.
c) 50 cm.
d) 240 cm.
e) 300 cm. - ANSWER e) 300 cm.
5. The mechanical test used to determine the ability of a material to resist failure by
brittle fracture
requires the use of:
a) A tensile test specimen.
b) A bend test specimen.
c) A compression test specimen.
, d) An impact test specimen.
e) A spectrographic test. - ANSWER d) An impact test specimen.
6. The cooling rate of aT-joint is:
a) Less than that in a butt joint.
b) Greater than that in a butt joint.
c) Greater than that in a butt joint only where the carbon equivalent is high .
d) Greater at the mid-section than at the start.
e) Greater at the mid-section than at the finish. - ANSWER b) Greater than that in a butt
joint.
10. If there is inadequate penetration at the root of a double vee groove, which of the
following
statements best defines the reason for this:
a) Groove angle exceeds specified amount.
b) Root opening too large.
c) Groove depth too large causing melt through on the second side
d) Groove angle is too small.
e) Excessive plate thickness. - ANSWER d) Groove angle is too small
11. The continuous method of magnetic particle inspection means:
a) Carrying out all the steps in the process without pause.
b) Using DC current.
c) Applying magnetic particles to the weld while the current is flowing in the yoke.
d) Applying magnetic particle to the test surface while current flows from one leg of the
yoke
through the material to the other leg of the yoke.
e) Precautions must be taken to prevent over-magnetization of the material. - ANSWER
c) Applying magnetic particles to the weld while the current is flowing in the yoke.
12. From the welding problems identified below which one of the five does not fit the
pattern established
by the other four?
a) Insufficient throat.
b) Incorrect bevel angle.
c) Loss of shielding gas.
d) Improper fit up.
e) Use of wrong consumable. - ANSWER a) Insufficient throat.
13. A 10 mm fillet weld has a nominal:
a) Throat dimension of 10 mm.
CORRECT AND UPDATED!!
,1. Which is not a recommended method for surface cleaning of a part for liquid
penetrant examination?
a) Cleaning with organic solvents.
b) Blasting with shot or dull sand.
c) Cleaning with de-greasers.
d) Use of de-scaling solutions.
e) Ultrasonic cleaning methods. - ANSWER b) Blasting with shot or dull sand.
2. Which of the following weld defects is most likely to be missed by radiography in a
weld:
a) Undercutting.
b) Porosity.
c) Slag inclusions.
d) Cracking.
e) Burn through . - ANSWER d) Cracking.
3. In the choices given below, metallographic tests would be the least informative with
regard to the:
a) Presence of the non-metallic inclusions.
b) Grain structure in the weld and fusion zone.
c) Ability of the material to withstand repeated fluctuating loads.
d) Extent and structure of the heat affected zone.
e) Number of weld passes. - ANSWER c) Ability of the material to withstand repeated
fluctuating loads.
4. In producing a drawing for a scale of 1:50, what would be the distance represented
by a distance on
the drawing of 6 em?
a) 12 cm.
b) 30 cm.
c) 50 cm.
d) 240 cm.
e) 300 cm. - ANSWER e) 300 cm.
5. The mechanical test used to determine the ability of a material to resist failure by
brittle fracture
requires the use of:
a) A tensile test specimen.
b) A bend test specimen.
c) A compression test specimen.
, d) An impact test specimen.
e) A spectrographic test. - ANSWER d) An impact test specimen.
6. The cooling rate of aT-joint is:
a) Less than that in a butt joint.
b) Greater than that in a butt joint.
c) Greater than that in a butt joint only where the carbon equivalent is high .
d) Greater at the mid-section than at the start.
e) Greater at the mid-section than at the finish. - ANSWER b) Greater than that in a butt
joint.
10. If there is inadequate penetration at the root of a double vee groove, which of the
following
statements best defines the reason for this:
a) Groove angle exceeds specified amount.
b) Root opening too large.
c) Groove depth too large causing melt through on the second side
d) Groove angle is too small.
e) Excessive plate thickness. - ANSWER d) Groove angle is too small
11. The continuous method of magnetic particle inspection means:
a) Carrying out all the steps in the process without pause.
b) Using DC current.
c) Applying magnetic particles to the weld while the current is flowing in the yoke.
d) Applying magnetic particle to the test surface while current flows from one leg of the
yoke
through the material to the other leg of the yoke.
e) Precautions must be taken to prevent over-magnetization of the material. - ANSWER
c) Applying magnetic particles to the weld while the current is flowing in the yoke.
12. From the welding problems identified below which one of the five does not fit the
pattern established
by the other four?
a) Insufficient throat.
b) Incorrect bevel angle.
c) Loss of shielding gas.
d) Improper fit up.
e) Use of wrong consumable. - ANSWER a) Insufficient throat.
13. A 10 mm fillet weld has a nominal:
a) Throat dimension of 10 mm.